5.4 Silicate Minerals

Silicon and oxygen bond covalently to create a silicate tetrahedron (SiO44-), which is a four-sided pyramid shape with oxygen at each corner and silicon in the middle (Figure 5.21). This structure is the building block of many important minerals in the crust and mantle. Silicon has a charge of +4, and oxygen has a charge of -2, so the total charge of the silicate anion is -4.

 

three spheres labelled "oxygen" are arranged in a triangle pattern. A smaller sphere labeled "silicon" is nestled on top of them. A fourth oxygen sits on top of the silicon sphere.Label: SiO4 4- Silicate tetrahedron
Figure 5.21 The silica tetrahedron is the building block of all silicate minerals. Source: Karla Panchuk (2018), CC BY-SA 4.0. Modified after Helgi (2013), CC BY-SA 3.0. View source.

In silicate minerals, these tetrahedra are arranged and linked together in a variety of ways, from single units to chains, rings, and more complex frameworks.  In the rest of this section we will look at the structures of the most common silicate minerals in Earth’s crust and mantle.

 

Make Your Own Tetrahedron

Figure 5.22 Pattern for a tetrahedron. Source: Steven Earle (2015), CC BY 4.0. View source.

Download this PDF file with the tetrahedron pattern shown here. Cut around the outside of the shape (solid lines and dotted lines), and then fold along the solid lines to form a tetrahedron.

If you have glue or tape, secure the tabs to the tetrahedron to hold it together. If you don’t have glue or tape, make a slice along the thin grey line and insert the pointed tab into the slit.

If you’re feeling ambitious, make several tetrahedra and and use toothpicks through the corners to make the configurations discussed below.

Isolated Tetrahedra

The simplest silicate structure—that of the mineral olivine (Figure 5.23)—is composed of isolated tetrahedra bonded to iron and/or magnesium ions. In olivine, the –4 charge of each silica tetrahedron is balanced by two iron or magnesium cations, each with a charge of +2.

 

Left: A pattern of triangles (representing tetrahedra) with circles (representing cations) between them. The triangles do not touch. Right: Yellowish green crystals labelled "Olivine (Mg, Fe)2SiO4"
Figure 5.23 Olivine is a silicate mineral made of isolated silica tetrahedra bonded to Fe and Mg ions (left). Source: Karla Panchuk (2021), CC BY-SA 4.0. Click for more attributions.

Olivine can be pure Mg2SiO4 or pure Fe2SiO4, or a combination of the two, written as (Mg,Fe)2SiO4. Magnesium and iron can substitute for each other because they both have a charge of +2, and they are similar in size: magnesium cations have a radius of 0.73 Å, and iron cations have a radius of 0.62 Å [1].

While iron and magnesium ions are similar in size, allowing them to substitute for each other in some silicate minerals, the common ions in silicate minerals come in a wide range of sizes (Figure 5.24).  Ionic radii are critical to the composition of silicate minerals, because the structure of the silicate mineral will determine the size of spaces available.

 

Anion: oxygen with a -2 charge and a radius of 1.4 Angstroms. Cations: K (+1, 1.37 A); Na (+1, 0.99 A); Ca (+2, 1 A); Mg (+2, 0.72 A); Fe (+2, 0.63 A); Fe (+3, 0.49 A); Si (+4, 0.26 A); C (+4, 0.15 A)
Figure 5.24 The ionic radii in angstroms of some of the common ions in silicate minerals. Radii shown to scale. Notice that iron appears twice with two different radii. This is because iron can exist as a +2 ion (if it loses two electrons when it becomes an ion) or a +3 ion (if it loses three). Fe2+ is known as ferrous iron. Fe3+ is known as ferric iron. Source: Karla Panchuk (2021), CC BY 4.0. Modified after Steven Earle (2015), CC BY 4.0 View source.

Chain Silicates

The mineral pyroxene is an example of a single-chain silicate (Figure 5.25), where one oxygen from each tetrahedron is shared with the next tetrahedron. Sharing means that fewer oxygens are needed to make the tetrahedra, so there’s less oxygen in this structure over all compared to olivine. This can be expressed as a silicon-to-oxygen ratio (Si:O). In olivine, tetrahedra aren’t connected directly to each other, so each silicon atom must have four oxygen atoms all to itself to complete a tetrahedron. That’s a ratio of 1:4. In pyroxene, each silicon atom only needs three unique oxygen atoms because it can borrow one from a neighbour to have a tetrahedron. For pyroxene, the Si:O is 1:3. With one less oxygen in the mix per tetrahedron, the net charge per silicon atom that must be balanced by cations is lower (-2 instead of -4).

 

Figure 5.25 Pyroxene (dark mineral in the photo) is a silicate mineral in which tetrahedra are linked in strings, with adjacent tetrahedra sharing an oxygen atom. Source: Karla Panchuk (2021), CC BY-SA 4.0. End-on view modified after Klein & Hurlbut (1993). Click for more attributions.

The way tetrahedra share oxygens in single-chain silicates is why, even though pyroxene is built out of silicate tetrahedra (with the silicate anion being SiO44-), its formula has the tetrahedra represented as SiO3 (e.g., MgSiO3, FeSiO3, and CaSiO3[2], or a multiple thereof). In other words, pyroxene has one cation for each silica tetrahedron (e.g., MgSiO3) while olivine has two (e.g., Mg2SiO4).

The structure of pyroxene is also more “permissive” than that of olivine, meaning cations with a wider range of ionic radii can fit into it. That’s why pyroxenes can have calcium cations (radius 1.00 Å) substitute for iron (0.63 Å) and magnesium (0.72 Å).

The mineral amphibole is also a chain silicate, but the the silica tetrahedra are linked in a double chains (Figure 5.26). Amphibole has a silicon-to-oxygen ratio higher than that of pyroxene, and hence still fewer cations are necessary to balance the charge. Amphibole is even more permissive than pyroxene, and its compositions can be very complex.
Figure 5.26 Amphibole (dark mineral in the photo) is a silicate mineral in which tetrahedra are linked in doubled-up strings. Tetrahedra share two oxygen atoms with adjacent tetrahedra. End-on view modified after Klein & Hurlbut (1993). Source: Karla Panchuk (2021), CC BY-SA 4.0. Click for more attributions.
Can You Find the Silicon to Oxygen Ratios?

Sheet Silicates

In mica structures, the silica tetrahedra are arranged in continuous sheets (Figure 5.27), where each tetrahedron shares three oxygen anions with adjacent tetrahedra. Because even more oxygens are shared between adjacent tetrahedra, fewer charge-balancing cations are needed for sheet silicate minerals.

Bonding between sheets is relatively weak, and this accounts for the tendency of mica minerals to split apart in sheets (Figure 5.27 bottom right). Two common micas in silicate rocks are biotite (Figure 5.27 bottom left), which contains iron and/or magnesium, making it a dark mineral; and muscovite (Figure 5.27 right), which contains aluminum and potassium, and is light in colour. All of the sheet silicate minerals have water in their structure, in the form of the hydroxyl (OH-) anion.

 

Figure 5.27 Micas are sheet silicates and split easily into thin layers along planes parallel to the sheets. Biotite mica (lower left) is has Fe and Mg cations. Muscovite mica (lower right) has Al and K instead. The muscovite mica shows how thin layers can split away in a sheet silicate. Source: Karla Panchuk (2018), CC BY-NC-SA 4.0. Top left- Modified after Steven Earle (2015), CC BY 4.0. Top right- Modified after Klein & Hurlbut (1993). Click for more attributions.

Some sheet silicates typically occur in clay-sized fragments (i.e., less than 0.004 mm). These include the clay minerals kaolinite, illite, and smectite, which are important components of rocks and especially of soils.

Framework Silicates

In framework silicates, tetrahedra are connected to each other in three-dimensional structures rather than in two-dimensional chains and sheets.

Feldspar

Feldspars are a group of very abundant framework silicates in Earth’s crust. They include alumina tetrahedra as well as silicate tetrahedra. In alumina tetrahedra, there is an aluminum cation at the centre instead of a silicon cation.

Feldspars are classified using a ternary (3-fold) system with three end-members (“pure” feldspars). This system is illustrated with a triangular diagram that has each end-member at one corner (Figure 5.28). The distance along a side of the diagram represents the relative abundance of the composition of each end-member.

Figure 5.28 Ternary diagram showing the feldspar group of framework silicate minerals. Alkali feldspars are those with compositions ranging between albite (with a Na cation) and orthoclase and its polymorphs (with a K cation. Plagioclase feldspars are those with compositions ranging between albite and anorthite (with a Ca cation). Source: Karla Panchuk (2018) CC BY-SA 4.0. Ternary diagram modified after Klein & Hurlbut (1993). Click for more attributions and a ternary diagram without mineral images.

One end-member is potassium feldspar (also referred to as K-feldspar), which has the composition KAlSi3O8. Depending on the temperature and rate of cooling, K-feldspar can occur as one of three polymorphs: orthoclase, sanidine, or microcline.  Another end member is albite, which has sodium instead of potassium (formula NaAlSi3O8). As is the case for iron and magnesium in olivine, there is a continuous range of compositions (referred to as a solid-solution series) between albite and orthoclase. Feldspars in this series are referred to as alkali feldspars. Potassium cations are much larger than sodium cations (1.37 Å versus 0.99 Å, respectively), so high temperatures are required to form alkali feldspars with intermediate compositions.

The third end-member is anorthite and it has calcium instead of potassium or sodium (formula CaAl2Si2O8). Feldspars in the solid-solution series between albite and anorthite are called plagioclase feldspars. Calcium and sodium cations are nearly the same size (1.00 Å and 0.99 Å, respectively), so from that perspective it makes sense that they substitute readily for each other, and that any intermediate compositions between CaAl2Si2O8 and NaAlSi3O8 can exist. However, calcium and sodium ions don’t have the same charge (Ca2+ versus Na+), making it surprising that they substitute so easily. The difference in charge is accommodated by substituting some Al3+ for Si4+.  Albite has one Al and three Si in its formula, while anorthite is has two Al and two Si.  Plagioclase feldspars of intermediate composition also have intermediate proportions of Al and Si.

Quartz

Quartz (SiO2; Figure 5.29) contains only silica tetrahedra. In quartz, each silica tetrahedron is bonded to four other tetrahedra (with an oxygen shared at every corner of each tetrahedron), making a three-dimensional framework.  As a result, the ratio of silicon to oxygen is 1:2. Because the one silicon cation has a +4 charge and the two oxygen anions each have a –2 charge, the charge is balanced. There is no need to add cations to balance the charge. The hardness of quartz and the fact that it breaks irregularly (notice the bottom of the crystal in Figure 5.29 right) and not along smooth planes result from the strong covalent/ionic bonds characteristic of the silica tetrahedron.

 

Figure 5.29 Quartz is another silicate mineral with a three-dimensional framework of silica tetrahedra. Sometimes quartz occurs as well-developed crystals (left), but it also occurs in common rocks such as granite (right). In addition to quartz, the granite contains potassium feldspar, albite, and amphibole. Source: Karla Panchuk (2018) CC BY-NC-SA 4.0. Click for more attributions.

Practice with Silicate Minerals & Their Structures

Click here to download a printable version of this exercise.

References

Klein, C. & Hurlbut, C. S., Jr. (1993). Manual of Mineralogy (after J. D. Dana). New York, NY: John Wiley & Sons, Inc.


  1. Å stands for Ångstrom, a unit commonly used to express atomic-scale dimensions. One angstrom is 10–10 m or 0.0000000001 m.
  2. The variation in composition can also be written as (Mg,Fe,Ca)SiO3, where the elements in the brackets can be present in any proportion.

License

Icon for the Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License

Physical Geology - H5P Edition V1.1 Copyright © 2021 by Karla Panchuk is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License, except where otherwise noted.